Method for stabilizing an engine coolant concentrate and preventing hard water salt formation upon dilution

ABSTRACT

Disclosed is a stabilized concentrate comprising least one stabilizer selected from the group consisting of polyacrylate polymers of the formula: 
     
       
         
         
             
             
         
       
     
     where R 1  is H; R 4  is a terminating group; X is 
     
       
         
         
             
             
         
       
         
         
           
             and R 2  and R 3  are each independently hydrogen, an alkali metal or an alkaline earth metal, and the sum of m and n provide a number average equivalent weight of less than 6500, and a number average molecular weight of less than 6500. The concentrate comprises 90 or more wt % freezing point depressant. The stabilized coolant concentrate can be diluted with water to provide a final coolant composition.

CROSS REFERENCE TO RELATED APPLICATION

The application is a continuation of U.S. patent application Ser. No.11/464,356 filed on Aug. 14, 2006 which claims the benefit of U.S.Provisional application Ser. No. 60/707,589, filed Aug. 12, 2005. Thecontents of both of the aforementioned applications are incorporatedherein by reference thereto.

FIELD OF THE INVENTION

The invention is directed to the stabilization of coolants for internalcombustion engines. More particularly, the invention is directed towardthe stabilization of engine coolant concentrates and the prevention ofhard water salt formation upon dilution of the stabilized engine coolantconcentrate with hard water.

BACKGROUND OF THE INVENTION

Automobile engine cooling systems contain a variety of metals, includingcopper, solder, brass, steel, cast iron, and aluminum. The possibilityof corrosive attack on such metals is high, due to the presence ofvarious ions as well as the high temperatures, pressures, and flow ratesfound in such cooling systems. The presence of corrosion products withinthe cooling system can interfere with heat transfer from the enginecombustion chambers, and may subsequently cause engine overheating andengine component failure due to excess metal temperatures.

To prevent these problems, a variety of organic and inorganiccompositions have been employed as corrosion inhibitors in enginecoolant formulations. Illustrative examples of corrosion inhibitors usedin engine coolant formulations include silicates, phosphates, organicacids and their salts, azole type compounds, molybdenum, nitrates,nitrites, borates, and the like, as well as combinations thereof.

However, many engine coolant formulations experience a variety ofproblems commonly attributed to the presence of corrosion inhibitors.Coolants are often provided in the form of concentrates that must bediluted with water prior to use in an automobile engine cooling system.

In some cases, engine coolant concentrates exhibit instability issuesafter extended warehouse or shelf storage. One common manifestation ofstorage instability in a coolant concentrate is inhibitor fallout in theform of precipitates. Corrosion inhibitors that are no longer part of ahomogenous coolant concentrate will be unavailable in the dilutedcoolant. A diluted coolant made from an unstable concentrate will thusprovide an engine with less corrosion protection.

Another problem encountered with engine coolant concentrates involvesthe water used for dilution. In many areas the only water available forsuch use is hard water, or water that contains appreciable levels ofdissolved salts. Hardness of water is a function of the concentration ofdissolved calcium and magnesium salts contained in the water, and isusually expressed in terms of a concentration (ppm) as CaCO₃ TotalHardness. Hard water as used herein refers to water having greater than150 ppm CaCO₃ total hardness. In many cases, the use of hard water forthe dilution of coolant concentrates results in a coolant that hasadverse effects upon the overall cooling system.

For example, EP 0 245 557 B1 discloses that the use of hard water todilute antifreeze/coolant formulations containing alkali metal silicateand borate corrosion inhibitors causes the formation of insoluble alkaliearth metal silicate flocs which precipitate from the antifreeze-watersolution. The resulting metal silicate flocs are said to be calciumand/or magnesium silicate salts that adversely affect the cooling systemfor several reasons. First, since the precipitates are alkali earthmetal silicate flocs, a rapid deletion of silicate in solution occurs;thus the corrosion-inhibiting properties of the formulation aredepleted. Moreover, the precipitating solids can eventually plug thepassages of the engine cooling system. Second, the formation of hardwater scale is undesirable because it can interfere with heat transferfrom the engine combustion chambers, and subsequently may cause engineoverheating and engine component failure due to excess metaltemperatures. EP 0 245 557 B1 discloses the use of phosphinopolycarboxylic acid/polycarboxylate compositions, or mixtures thereof asstabilizers to prevent the precipitation of insoluble alkali earth metalsilicate and borate corrosion inhibitors where said formulations arediluted with hard water.

However, EP 0 245 557 B1 is limited to the prevention of hard watersalts in coolants having only certain corrosion inhibitors. Moreover,none of the prior art has simultaneously resolved the dual problems ofcoolant concentrate storage stability and the formation of hard watersalt formation upon dilution of the concentrate with hard water.

Accordingly, there continues to be a need for the stabilization ofcoolant concentrates for internal combustion engines.

More particularly, there continues to be a need for methods andcompositions directed toward the prevention of the formation of hardwater salts upon dilution of engine coolant concentrates with hardwater.

Most particularly, there continues to be a need for methods andcompositions directed toward the simultaneous stabilization of coolantconcentrates and the prevention of hard water salt formation upondilution of a stabilized engine coolant concentrate with hard water.

SUMMARY OF THE INVENTION

The invention provides coolant concentrates stabilized with a particularstabilizer additive. It has unexpectedly been found that coolantconcentrates stabilized with at least one of the particularly identifiedstabilizers have improved shelf stability, particularly in regards toshelf stability at elevated temperatures.

In addition, it has unexpectedly been found that the particularlystabilized coolant concentrates can be diluted with hard water toprovide a coolant that fails to form hard water salts.

Disclosed is a coolant concentrate comprising one or more corrosioninhibitors and at least one stabilizer selected from the groupconsisting of polyacrylate polymers of the formula:

where R₁ is H; R₄ is H, hydroxyl, alkyl, or another terminating group; Xis

and R₂ and R₃ are each independently hydrogen, an alkali metal or analkaline earth metal, and the sum of m and n provide a number averageequivalent weight of less than 6500, wherein the coolant concentratecomprises at least 90 wt % glycol, based on the total weight of thecoolant concentrate.

Also disclosed is a method for preventing hard water salt formation upondilution of a coolant concentrate with hard water, comprising dilutingthe disclosed concentrate with hard water to provide a final coolantcomprising at least 75 wt % water.

A method of stabilizing a coolant is also disclosed, the methodcomprising adding to a coolant at least one stabilizer selected from thegroup consisting of polyacrylate polymers of the formula:

where R₁ is H; R₄ is H, hydroxyl, alkyl, or another terminating group; Xis

and R₂ and R₃ are each independently hydrogen, an alkali metal or analkaline earth metal, and the sum of m and n provide a number averageequivalent weight of less than 6500, and a number average molecularweight of less than 6500.

Finally, a method of stabilizing an engine coolant concentrate andpreventing hard water salt formation upon dilution of the coolantconcentrate with hard water is disclosed, comprising adding to a coolantconcentrate at least one stabilizer of the formula:

where R₁ is H; R₄ is H, hydroxyl, alkyl, or another terminating group; Xis

and R₂ and R₃ are each independently hydrogen, an alkali metal or analkaline earth metal, and the sum of m and n provide a number averageequivalent weight of less than 6500, the concentrate comprising at least90 wt % glycol to provide a stabilized coolant concentrate, and dilutingthe stabilized coolant concentrate with hard water to provide a finalcoolant having an initial concentration of hard water salt insolubleprecipitates of less than 50 ppm.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The disclosed coolant concentrates generally comprise a freezingpoint-depressing agent in range of about 90% to 99% by weight; coolantcorrosion inhibitors; the disclosed stabilizers; and optionally othercoolant additives, such as antifoam agents, colorants, dispersants,anti-scaling agents, wetting agents, pH adjusting and buffering agentsand the like.

The freezing point depressant suitable for use includes alcohol ormixture of alcohols, such as monohydric or polyhydric alcohols andmixture thereof. In one embodiment, the freezing point depressant willbe polyhydric alcohol, especially a mixture of polyhydric alcohols.

Illustrative examples of suitable freezing point depressants includemethanol, ethanol, propanol, butanol, furfurol, furfuryl alcohol,tetrahydrofurfuryl alcohol, ethoxylated furfuryl alcohol, ethyleneglycol, diethylene glycol, triethylene glycol, 1,2-propylene glycol,1,3-propylene glycol, dipropylene glycol, butylene glycol, glycerol,glycerol-1,2-dimethyl ether, glycerol-1,3-dimethyl ether, monoethyletherof glycerol, sorbitol, 1,2,6-hexanetriol, trimethylopropane, alkoxyalkanols such as methoxyethanol and mixtures thereof.

In one embodiment, the freezing point depressant will be at least one ofethylene glycol, diethylene glycol, 1,2-propylene glycol, 1,3-propyleneglycol and combinations comprising one or more of the foregoing. In oneexemplary embodiment, the freezing point depressant will comprise acombination of one or more of ethylene glycol, diethylene glycol,1,3-propylene glycol and/or 1,2-propylene glycol.

In one embodiment, the freezing point depressant is present in thecoolant concentrate composition in an amount of about 90% to about 99.9%(by weight). In another embodiment, the freezing point depressant ispresent in the coolant concentrate in an amount of about 91% to 98%. Inone exemplary embodiment, the freezing point depressant is present inthe coolant concentrate in an amount of about 91% to about 95% byweight.

After dilution of the coolant concentrate, the freezing point depressantis present in the resulting coolant composition (also referred to hereinas a diluted coolant or final coolant) in an amount of less than 90% toabout 10%, based on the total weight of the coolant composition. Inanother embodiment, the freezing point depressant is present in thecoolant composition in an amount of from about 70% to 30%, based on thefinal weight of the coolant composition. In one exemplary embodiment,the freezing point depressant is present in the coolant composition,i.e., a diluted or final coolant, in an amount of about 60% to 40% byweight, based on the final weight of the coolant composition.

Coolants may differ in the type(s) of corrosion inhibitors added tothem. Conventional coolants may be based on silicate(s) as a primarycorrosion inhibitor. Extended life coolants may include organic acid(s)as a primary corrosion inhibitor. Hybrid coolants may be based on acombination of components from conventional and/or extended lifeantifreeze/coolants. In one embodiment, the corrosion inhibitors usefulin the disclosed coolant concentrates and coolant compositions includethose corrosion inhibitors known to be useful, and combinations thereof.Illustrative examples of suitable corrosion inhibitors generally includeorganic acids such as di-carboxylic acids, carboxylates, and saltsthereof; azole type compounds such as triazoles and thiazoles; andsilicates, phosphates, nitrates, nitrites, borates, benzoates,molybdates, or alkali metal or alkaline earth metal salts thereof andthe like, as well as combinations of two or more of the foregoing.

In one embodiment, the corrosion inhibitors employed in the disclosedcoolants and compositions will comprise at least one of silicates,phosphates, the alkali metal or alkaline earth metal salts thereof, andcombinations of two or more of the foregoing; as well as one or moreadditional corrosion inhibitors selected from the group consisting oforganic acids such as di-carboxylic acids, carboxylates, and saltsthereof; azole type compounds such as triazoles and thiazoles; nitrates;nitrites; borates; benzoates; molybdates; or alkali metal or alkalineearth metal salts thereof; and combinations of two or more of theforegoing additional corrosion inhibitors.

In one exemplary embodiment, the corrosion inhibitors employed in thedisclosed coolants and compositions will comprise a combination of (i)and (ii) wherein (i) is one or more silicates or the alkali metal oralkaline earth metal salts of one or more silicates and (ii) is one ormore phosphates or the alkali metal or alkaline earth metal salts of oneor more phosphate compounds; as well as one or more additional corrosioninhibitors selected from the group consisting of organic acids such asdi-carboxylic acids, carboxylates, and salts thereof; azole typecompounds such as triazoles and thiazoles; nitrates; nitrites; borates;benzoates; molybdates; or alkali metal or alkaline earth metal saltsthereof; and combinations of two or more of the foregoing additionalcorrosion inhibitors.

In one especially exemplary embodiment, the corrosion inhibitorsemployed in the disclosed coolants and compositions will comprise atleast one phosphate or the alkali metal or alkaline earth metal saltsthereof; as well as one or more additional corrosion inhibitors selectedfrom the group consisting of organic acids such as di-carboxylic acids,carboxylates, and salts thereof; azole type compounds such as triazolesand thiazoles; nitrates; nitrites; borates; benzoates; molybdates; oralkali metal or alkaline earth metal salts thereof; and combinations oftwo or more of the foregoing additional corrosion inhibitors.

Non-limitative examples of suitable organic acids include, but are notlimited to aliphatic and/or aromatic mono- and/or dicarboxylic acidssuch as 2-ethylhexanoic acid, benzoic acids, t-butyl benzoic acid,sebacic acids, nonanoic acids, dodecanoic acids, neodecanoic acids, andmixtures thereof.

Suitable carboxylates include saturated and unsaturated aliphatic, andaromatic mono-, di- and tricarboyxlic acids, and salts and isomersthereof, and any mixture thereof. Particularly, the suitablecarboxylates include C₄ to C₁₂ mono-, or di-carboxylic acids, such as2-ethyl hexanoic acid, neodecanoic acid, benzoic acid, t-butylbenzoicacid, dodecanediodic acid, and sebacic acid, or alkali and alkali earthmetal, ammonium and amine salts, or isomers and mixtures thereof.

For example, in one embodiment, illustrative examples of suitableorganic acids are acids such as 2-ethylhexanoic acid (“2-EHA”) orneo-octanoic acid, or isomers and/or salts thereof, and neo-decanoicacid, or isomers and/or salts thereof. As with neo-decanoic acid, 2-EHAand neo-octanoic acid are less expensive than sebacic acid and morereadily available (2-EHA may be obtained from, for example, ALLCHEMIndustries, Inc., ASHLAND Chemical Co., BASF Corp., Brook-Chem. Inc.,EASTMAN Chemical Group and Dow Chemical Corp.; neo-octanoic acid isavailable from, for example, Exxon Chemical Company). Also, thesemono-carboxylic acids are available as liquids rather than solids (as issebacic acid) and as such, they are more easily used to preparecorrosion inhibitors on a commercial scale.

In another embodiment, an illustrative organic acid is a cyclohexenoicacid component having the structure:

wherein each of R¹, R² and R³ is, independently, selected from the groupconsisting of H, OH, COOH, C¹-C¹⁰ alkyl groups, glycol esters, orcombinations thereof. Where the substituents comprise a C¹-C¹⁰ alkylgroup, more preferred alkyl groups have up to six carbon atoms becausesuch groups are believed to result in cyclohexenoic acids havingimproved miscibility in the antifreeze composition.

For the cyclohexenoic acid component, R¹ is preferably H or COOH (withCOOH more preferred), R³ preferably comprises a C₁-C₁₀ alkyl group, andR² preferably has the structure:

(CH₂)x-(COO)—[(C₂)y-O]z-H

wherein:x is from 0 to 10;y is from 1 to 5; andz is from 0 to 5.

Preferably, z is 0-2, more preferably z is 1 or 2, and even morepreferably z is 2. Examples of useful cyclohexenoic acids include:

The acid components of the corrosion inhibitors of this invention mayalternatively be in the form of an alkali metal salt, ammonium salt oramine salt. Preferred salts are the alkali metal salts, and mostpreferred are sodium or potassium salts of the mono-carboxylic acids.

In one embodiment, the disclosed coolant concentrates and coolantcompositions comprise compounds containing 5- or 6-member heterocyclicring as the active functional group, wherein the heterocyclic ringcontains at least one nitrogen atom, for example, an azole compound.Particularly, benzotriazole, tolyltriazole, methyl benzotriazole (e.g.,4-methyl benzotriazole and 5-methyl benzotriazole), butyl benzotriazole,and other alkyl benzotriazoles (e.g., the alkyl group contains from 2 to20 carbon atoms), mercaptobenzothiazole, thiazole and other substitutedthiazoles, imidazole, benzimidazole, and other substituted imidazoles,indazole and substituted indazoles, tetrazole and substitutedtetrazoles, and mixtures thereof can be used as corrosion inhibitors.

The azole compound or mixture may be present in the coolant concentratesin an amount of from about 1 ppm to about 8000 ppm, while in oneexemplary embodiment, they will be present in an amount of about 10 ppmto about 5000 ppm.

An illustrative example of a suitable silicate based corrosion inhibitoris an organosiloxane/silicate copolymer present in an amount of from0.01 percent to 10 percent by weight based upon the weight of thecoolant concentrate and consisting essentially of:

(1) from 0.1 to 99.9 parts by weight of at least one member selectedfrom the group consisting of (a) siloxane groups represented by theformula:

RSiO_(1.5)

wherein R is a member selected from the group consisting of the methyl,ethyl, propyl, phenyl and vinyl groups and (b) siloxane groupsrepresented by the formula:

wherein Y is a member selected from the groups consisting of halogencontaining groups, cyano containing groups, aryl containing groups,amino containing groups, glycidoxy containing groups, carboxy estercontaining groups, glycidoxy containing groups, mercapto containinggroups, hydroxy and polyhydroxy containing groups, and mixtures thereof,a is an integer having a value of at least 1, the group represented by Yis separated from the silicon atom by at least two successive carbonatoms, b is an integer having a value of from 1 to 3 inclusive, R′ is amonovalent hydrocarbon group, c is an integer having a value from 0 to 2inclusive, (b+c) has a value from 1 to 3 inclusive; and

(2) from 0.1 to 99.9 parts by weight of at least one silicate grouprepresented by the formula:

$\left\lbrack {M_{1/d}O} \right\rbrack_{e}{SiO}_{(\frac{4 - e}{2})}$

wherein M is a cation that forms a water soluble silicate, d is thevalence of the cation represented by M and has a value of at least 1 ande has a value from 1 to 3 inclusive, said parts by weight of said groupsin the copolymer being based on 100 parts by weight of the copolymer,the improvement comprising said composition additionally containing atleast one nitrate salt, in the absence of nitrate, in an amountsufficient to provide aluminum corrosion protection.

Typical “Y” substituents would include, for example, CF₃, CN, NH₂, Cl,COOH, SH, CH₂(O)CHCH₂(O), NH₂CH₂CH₂NH, CH₃OOC, CH₃COO, (CH₂CH₂O)_(n),CH₃OOCCH₂CH₂NHCH₂CH₂NH, carbohydrates, CH₂(OH)CH(OH), CH₂(OH)CH(OH)CH₂,

CH₂(OH)CH(OH)CH₂O, CH₂(OH)CH(OH)CH₂OCH₂CH(OH)CH₂O,CH₂(OH)CH₂OCH₂CH(OH)CH₂O, R″(OCH₂CH₂)_(n)(OC₃H₆)_(m)O andR″(OCH₂CH₂)_(n)(OC₃H₆)_(m)OCH₂CH(OH)CH₂O and the like, wherein R″ is amember selected from the group consisting of the monovalent hydrocarbonand the hydrogen atom, and n and m are integers having a value of from 0to 20 inclusive.

In another aspect of the invention, the above-describedorganosiloxane/silicate copolymer composition additionally contains from0.1 to 99.8 parts by weight of at least one siloxane group selected fromthe group consisting of the groups represented by the formula:

wherein R′″ is a monovalent hydrocarbon group other than the methyl,ethyl, propyl, phenyl and vinyl groups and R′ has the above-definedmeaning, said parts by weight of said groups in the copolymer beingbased on 100 parts by weight of the copolymer.

Illustrative examples of suitable phosphate compounds include thosecommonly known in the art such as phosphoric acid and the neutralizedsalts thereof. In one embodiment, the phosphate compound will comprisean alkaline earth metal salt or an alkali metal salt of phosphoric acid.In one exemplary embodiment, the phosphate compound will be sodiumphosphate or potassium phosphate. It will be appreciate that suchphosphate compounds may be added to the coolant concentrate or coolantcomposition directly in the salt form or prepared in situ via theaddition of the acid form, i.e., phosphoric acid, and an appropriateneutralizer such as sodium hydroxide or potassium hydroxide. In oneespecially exemplary embodiment, the corrosion inhibitors employed willcomprise phosphate compounds that are alkaline earth salts prepared insitu in either the coolant concentrate or coolant composition.

In one embodiment, the disclosed coolant concentrates and coolantcompositions comprise benzoates as corrosion inhibitors. Suitableexamples of benzoates for use as corrosion inhibitors include, but arenot limited to, alkaline earth metal benzoates such as sodium benzoateand potassium benzoate, ammonium benzoate, amine benzoates (e.g.diethylamine benzoate), cycloaliphatic amine benzoates (e.g.cyclohexylamine benzoate), and alkanolamine benzoates (e.g.triethenolamine benzoate). In one embodiment, the corrosion inhibitorswill comprise benzoates selected from the group consisting of sodiumbenzoate, potassium benzoate, and mixtures thereof.

In one embodiment, the corrosion inhibitors employed in the disclosedcoolants and compositions will comprise at least one of silicates,phosphates, the alkali metal or alkaline earth metal salts thereof, andcombinations of two or more of the foregoing. In one embodiment, thesilicates may be present in an amount of from 0.05 to 0.8% by weight,based on the total weight of the coolant concentrate, while in anotherembodiment, they will be present in an amount of from 0.1 to 0.5% byweight, based on the total weight of the coolant concentrate. In oneembodiment, the phosphates may be present in an amount of from 0.1 to1.2% by weight, based on the total weight of the coolant concentrate,while in another embodiment, they will be present in an amount of from0.3 to 0.7% by weight, based on the total weight of the coolantconcentrate.

In one embodiment, the total amount of all corrosion inhibitors presentin a coolant concentrate will be from about 0.1 to about 10% by weight,based on the total weight of the coolant concentrate. In anotherembodiment, the total amount of corrosion inhibitors present will befrom about 1 to about 8% by weight, based on the total weight of thecoolant concentrate. In one exemplary embodiment, the total amount ofcorrosion inhibitors present will be from about 2 to about 4% by weight,based on the total weight of the coolant concentrate.

The disclosed coolant concentrates and coolant compositions comprise atleast one stabilizer selected from the group consisting of certain acidfunctional or ionic group functional polyacrylate polymers. The term‘polyacrylate polymers’ as used herein refers to both homopolymers andcopolymers resulting from the free radical polymerization of acrylicacid and/or (meth)acrylic acid monomers. In the case of copolymers, theacrylic acid and/or (meth)acrylic acid monomers may be copolymerizedwith other unsaturated monomers, including alkyl esters, hydroxylsubstituted alkyl esters, and the like.

The stabilizers or stabilizing agents used herein will comprise acidgroups or the neutralized salt groups thereof, i.e., ionic groups. Inone exemplary embodiment, the stabilizing agents used herein willcomprise ionic groups. If acid functional stabilizing agents are used,an appropriate amount of neutralizing agent will be used to neutralizeat least 90% of the acid groups present, i.e., to convert the acidgroups to salt groups. In another embodiment, an appropriate amount ofneutralizing agent will be used to neutralize substantially all of acidgroups present in the stabilizing agent. In one exemplary embodiment,the functionalized form of the stabilizing agent is a neutralized salt,whether as added or as present in the concentrate after the addition ofa neutralizing agent.

In one embodiment, the stabilizing agents used will comprise ionicgroups comprising alkali metals or alkali earth metals. In oneembodiment, the stabilizing agent will comprise alkali metals. In oneexemplary embodiment, the stabilizing agent will comprise sodiumpolyacrylic acid polymers, i.e., polyacrylic acid polymers wherein theacid groups have been neutralized with a material such as sodiumhydroxide to provide sodium salts.

In one embodiment, the stabilizing agent will be of the formula:

where R₁ is H; R₄ is a terminating group; X is

and R₂ and R₃ are each independently hydrogen, an alkali metal or analkaline earth metal, and the sum of m and n provide a number averageequivalent weight of less than 6500.

The term “terminating group” as used herein refers to the residual groupresulting from the use of chain terminating agents in polymerizationreactions. Such compounds are commonly refers to as capping agents.Illustrative examples of such terminating groups include hydrogen;hydroxyl, alkyl groups, especially those having from 1 to 4 carbons; andalkoxy groups, especially those having from 1 to 3 carbons. In oneembodiment, R₄ will be either hydrogen or a hydroxyl group. In oneexemplary embodiment, R₄ will be either hydrogen or a hydroxyl group.

As indicated above, while R₂ and R₃ may be hydrogen, in one exemplaryembodiment, R₂ and R₃ will be either an alkaline earth metal or analkali metal. In one especially exemplary embodiment, R₂ and R₃ will bean alkali metal such as potassium or sodium.

It will be appreciated that when m is zero or X is of the formula

the stabilizing agent will be a homopolymer.

In one exemplary embodiment, the stabilizing agent will be of theformula:

wherein R₁, R₂, and R₄ are as defined above.

The stabilizing agents suitable for use herein may also be characterizedby a number average molecular weight of less than 6500. In anotherembodiment, the stabilizing agents suitable for use herein will have anumber average molecular weight of from about 1000 to about 4500. In oneexemplary embodiment, the stabilizing agents suitable for use hereinwill have a number average molecular weight of from about 2000 to about3400.

In general, the stabilizing agents may be used as 30 to 50% solutions inwater. Solutions of 30 wt % to 50 wt % of suitable stabilizing agentsemployed will generally have pHs of from 1.5 to 3.5. In one exemplaryembodiment, a solution of 30 wt % to 50 wt % of suitable stabilizingagent employed in the disclosed methods will have a pH of from 2.0 to3.3. It will be appreciated that in one exemplary embodiment, asdiscussed below, the acid forms of the stabilizing agents will beneutralized in situ to provide the alkaline earth metal salt or alkalisalt thereof.

Commercially available examples of suitable stabilizing agents includeAR-257, AR-900, AR-900A, AR-921A, and AR-335 from ALCO Chemical ofChattanooga Tenn. and Mayoquest 1500 or Mayoquest 1860 from VulcanChemical. In one exemplary embodiment, the disclosed coolantconcentrates and coolant compositions will comprise AR-335.

In one embodiment, the disclosed coolant concentrates will generallycomprise from 0.01 to 1.00 wt % of stabilizing agent, based on the totalweight of the coolant concentrate. In another embodiment, the disclosedcoolant concentrates will comprise from 0.01 to 0.50 wt % of stabilizingagent, based on the total weight of the coolant concentrate. In oneexemplary embodiment, the disclosed coolant concentrates will comprisefrom 0.05 to 0.20 wt % of stabilizing agent, based on the total weightof the coolant concentrate.

In one embodiment, the disclosed coolant compositions (i.e., theconcentrate plus sufficient water for dilution as discussed below) willgenerally comprise from 0.005 to 0.50 wt % of stabilizing agent, basedon the total weight of the coolant composition. In another embodiment,the disclosed coolant compositions will comprise from 0.005 to 0.25 wt %of stabilizing agent, based on the total weight of the coolantcomposition. In one exemplary embodiment, the disclosed coolantcompositions will comprise from 0.025 to 0.10 wt % of stabilizing agent,based on the total weight of the coolant composition.

The disclosed concentrates may be diluted with water to providecoolants. It is an aspect of the disclosed method that the water usedfor dilution need not be deionized water or softened water. Thus, in oneembodiment, the water used for dilution is hard water. Hard water asused herein refers to water having greater than 150 ppm CaCO₃ totalhardness.

The water is present in the disclosed coolant compositions, i.e., adiluted or final coolant, in an amount of about 1% to about 90% byweight in one embodiment, while in another embodiment, the water will bepresent in an amount of from about 30% to 70%, all based on the totalweight of the coolant composition. In one exemplary embodiment, thewater will be present in the disclosed coolants in an amount of about40% to about 60% by weight, based on the total weight of the coolantcomposition.

It will be appreciated that the disclosed method is advantageous becausethe stabilized coolant concentrate can be diluted with hard water toprovide a final coolant having an initial concentration of hard watersalt insoluble precipitates that is less than would be seen without theuse of the disclosed stabilizing agents and stabilized concentrates. Inone embodiment, the disclosed method comprises diluting the stabilizedcoolant concentrate with hard water to provide a final coolant having aninitial concentration of hard water salt insoluble precipitates of lessthan 50 ppm. “Initial concentration of hard water salt insolubleprecipitates” as used herein refers to the amount of hard water saltinsoluble precipitate formed within one to two hours of the hard wateraddition. In this embodiment, hard water refers to water having from 150to 500 ppm CaCO₃ total hardness and an amount of stabilizer agent withinthe ranges discussed above. However, it will be appreciated that hardwater with a hardness greater than 500 ppm CaCO₃ total hardness can beused with increasing amounts of the above disclosed stabilizing agents.

As discussed above, the final coolant composition will generallycomprise a buffer or neutralizing agent sufficient to provide a final pHof from 7.0 to 11.0. In one embodiment, the buffer or neutralizing agentwill be added in amount sufficient to provide a final pH of from 7.0 to10.0. In one embodiment, the buffer or neutralizing agent will be addedin amount sufficient to provide a final pH of from 8.0 to 10.0.Illustrative examples of common buffers and/or neutralizing agents arealkali metal hydroxides such as sodium hydroxide or potassium hydroxide.

Other optional additives that may be present in commercialantifreeze/coolants include, but are not limited to: wetting agents andsurfactants such as, for example, ionic and/or non-ionic surfactantssuch as the poly(oxyalkylene) adducts of fatty alcohols; defoamersand/or lubricants such as polysiloxanes and polyoxyalkylene glycols; andother ingredients suitable for antifreeze/coolants that do not adverselyaffect the antifreeze/coolant characteristics sought to be achieved bythe end use of the antifreeze/coolant.

Experimental data showing the benefits of using the instant inventionare described in the example below.

Example 1 Part A Anti-Scaling Testing

In order to study the ability of the additives to function as ananti-scale agent a test method had to be developed to determine theireffectiveness to stop the formation of scale in the presence of hardwater. It was decided to test these materials as anti-scaling agent by amodified compatibility test outlined in Section 4.10 of General Motorsspecification GM6227M.

GM6227M Section 4.10 provides that samples of the coolant concentrateshall show no separation or precipitation when diluted with a synthetichard water and tested as follows: prepare the hard water by adding 0.275g of CaCl₂ to 1 L of the synthetic water described in ASTM D1384; mix100 mL of the coolant concentrate plus 100 mL of the synthetic water(room temperature) in a 250 mL beaker, and allow to stand in the dark 24h; make a second mixture, as above, heat to 82° C. and allow to cool toroom temperature and to stand in the dark 24 h. Slight cloudiness ispermitted; but formation of a precipitate is considered sufficient tointerfere with bulk storage and use of the mixtures.

In the modified tests, the total hardness level used was twice the levelgiven in the GM 6277M test method in order to look at worst case.

The results of the modified GM test at room temperature show thecontrol, Coolant A, to give a precipitate. Coolant A is a conventionalNorth American coolant comprising both silicate and phosphate corrosioninhibitors as well as additional inorganic acid based corrosioninhibitors.

Turning to the last two columns of Table 1, it can be seen thatAlcosperse 124, Alcosperse 125, Alcosperse 725, Aquatreat AR-241, VersaTL-4, Versa TL-77 and Mayoquest C-100 gave similar results. These fluidswere not further tested per the modified GM test at the highertemperature, 82° C. Narlex LD29, Narlex LD41, Alcosperse 149, Alcosperse177, Alcosperse 408, Alcosperse 602-N, Aquatreat AR-4, Aquatreat AR-545,Aquatreat AR-550, Aquatreat AR-900-A, Aquatreat AR-921-A, AquatreatAR-980, Mayoquest 1320 and Mayoquest 2100 showed no signs of precipitatebut the fluid did become very slightly turbid as compared to theoriginal solution. The Narlex LD30, Alcosperse 240, Alcosperse 420,Aquatreat AR-257, Aquatreat AR-335, Aquatreat AR-546 and Mayoquest 1500showed no change and no sign of precipitate or turbidity.

All of the materials that showed no signs of precipitate were thentested at 82° C. The only material that behaved similar to the controlwas Mayoquest 2100. However, Mayoquest 1500 showed signs of heavyprecipitate after 5 days. The modified GM test results are shown belowin the last two columns of Table 1.

Part B General Stability

The effect, if any, of these materials on the general stability of theantifreeze concentrate and their overall compatibility (long term) andsolubility was evaluated as follows. The stabilizing agents were alladded to the control antifreeze at the level (0.1 wt %) for long termstability. The results are set forth in Table 2 which provides the 4month storage stability results for various additives with the controlantifreeze at three different temperature (Room temperature=RT, 130° F.,and 100° C.).

Coolant A was again used as a control. At room temperature all of thematerials tested exhibited the same stability as the control. All thesame remained homogenous (no separation or discoloration).

After 3 months at 130° F. the control showed a very slight whiteprecipitate at the bottom of the sample. All of the samples containingthe various additives were stable showing no signs of precipitation,separation or discoloration after 4 months.

At 100° C., the control showed a heavy precipitate after 24 hours. Manyof the samples containing the additives show a similar behavior.

Alcosperse 149, Mayoquest 1320 and Mayoquest 2100 did not formprecipitates until 48 hours.

Alcosperse 420, Aquatreat AR-257, Aquatreat AR-335, Aquatreat AR-900-A,Aquatreat AR-921-A, Mayoquest 1500 and Mayoquest 1860 did not start toshow any sign of precipitation until 5 days or longer (see chart fordetails on each materials). Heavier precipitate was not noticed until 9days in some cases. The Mayoquest 1860 color shifted (to a light brownafter 12 days) and a precipitate formed after 21 days. The Alcosperse420 did not change after day 5. Mayoquest 1500 showed no signs ofprecipitation over the 4-month test.

The test results show that some of these additives had the uniqueability of stabilizing inhibitor package in the antifreeze concentratefrom precipitating out at evaluated temperature. The precipitation ofinhibitor package has posed a problem for the antifreeze concentratewhen stored in warehouse in the hot summer months and in othersituations of long-term storage. Once inhibitors fallout it is sometimeshard to get them back into solution. Any fallout of inhibitors resultsin a decreased amount of active inhibitors in the antifreeze and candestabilize the whole inhibitor package.

The addition of these stabilizer materials provides a way a preventingthis from happening and ensuring the correct concentration of a stableinhibitor package is available when the coolant is diluted for use.

Part C Additional Test Results

In order to evaluate the effect these materials might have on otherperformance requirements of the engine coolant, several of thecandidates were tested in corrosion tests (ASTM tests) developed by theautomotive industry. The results of the testing are also set forth inthe bottom portion of Table 2. The results show the additives are notadversely affecting the performance of the antifreeze as compared to thecontrol, Coolant A.

In addition to the ASTM testing, some in-house testing of somecandidates formulas were conducted in an MTU-HSSD test unit. This testlooks at the ability of the additives to prevent scale build-up in thetest unit. The results obtained from the unit to date are also set forthin the bottom portion of Table 2.

TABLE 1 ANTI-SCALING ADDITIVE TESTS 4-MONTH RESULTS GM RT GM 82 C.Stabilizing Agent RT 130 F. 100 C. Hard Hard Added to Coolant AStability* Stability* Stability H2O H2O Control - No ok @16 wk sl wispyppt (24 hr) ppt Mod ppt Stabilizing Agent ppt(7 wk) Narlex LD29 ok @8 wkok @8 wk ppt (24 hr) sl turb v sl ppt Narlex LD30 ok @8 wk ok @8 wk ppt(24 hr) clr v sl ppt Narlex LD41 ok @8 wk ok @8 wk ppt (24 hr) sl turb vsl ppt Alcosperse 124 ok @8 wk ok @8 wk ppt (24 hr) ppt Alcosperse 125ok @8 wk ok @8 wk ppt (24 hr) sl turb v sl ppt Alcosperse 149 ok @8 wkok @8 wk ppt (48 hr) sl turb Alcosperse 177 ok @8 wk ok @8 wk ppt (24hr) sl turb v v sl ppt, sl turb Alcosperse 240 ok @8 wk ok @8 wk ppt (24hr) clr v v sl ppt, clear Alcosperse 408 ok @8 wk ok @8 wk ppt (24 hr)sl turb v sl ppt Alcosperse 420 ok @16 wk ok @16 wk lint(5 days) clr v vsl ppt, sl turb Alcosperse 602-N ok @8 wk ok @8 wk ppt (24 hr) sl turb vv sl ppt, clear Alcosperse 725 ok @8 wk ok @8 wk ppt (24 hr) pptAquatreat AR-4 ok @8 wk ok @8 wk ppt (24 hr) sl turb v sl ppt AquatreatAR-241 ok @8 wk ok @8 wk ppt (24 hr) ppt Aquatreat AR-257 ok @16 wk ok@16 wk lint(5 days)/ clr v sl ppt ppt(9 days) Aquatreat AR-335 ok @16 wkok @16 wk lint(5 days)/ clr v v sl ppt, ppt(12 days) clear AquatreatAR-545 ok @8 wk ok @8 wk ppt (24 hr) sl turb v sl ppt Aquatreat AR-546ok @8 wk ok @8 wk ppt (24 hr) clr v sl ppt Aquatreat AR-550 ok @8 wk ok@8 wk ppt (24 hr) sl turb v v sl ppt, clear Aquatreat AR-900-A ok @16 wkok @16 wk lint(5 days)/ sl turb v v sl ppt, ppt(9 days) clear AquatreatAR-921-A ok @16 wk ok @16 wk lint(5 days)/ sl turb v v sl ppt, ppt (9days) clear Aquatreat AR-980 ok @8 wk ok @8 wk ppt (24 hr) sl turb v slppt Versa TL-4 ok @8 wk ok @8 wk ppt (24 hr) ppt Versa TL-77 ok @8 wk ok@8 wk ppt (24 hr) ppt Mayoquest C-100 ok @8 wk ok @8 wk ppt (24 hr) pptMayoquest 1320 ok @8 wk ok @8 wk ppt (48 hr) sl turb v v sl ppt, sl turbMayoquest 1500 ok @16 wk ok @16 wk clr v sl ppt/ svr ppt Mayoquest 1860ok @16 wk ok @16 wk color shift v v sl ppt, (12 days) clear Mayoquest2100 ok @8 wk ok @8 wk ppt (48 hr) sl turb mod ppt *Those samples thatfailed the 100 C. and GM Hard H₂O tests had their RT and 130 F. teststerminated after eight weeks. **Hard H₂O tests run according to theGM6277M:R1:ETSGJD test method (except salt level doubled).

TABLE 2 Overview of Anti-Scaling Additive Testing Control - Coolant AAquatreat Aquatreat w/o Stabilizing Agent Alcosperse 420 AR-257 AR-335RT Stability ok ok ok ok 130 F. Stability ok ok ok ok 100 C. phos, ppt,moderate moderate no gels gel gel GM Hard Water Test sl, ppt ok ok ok(RT) GM Hard Water Test mod ppt v sl ppt, sl v sl ppt v v sl ppt (82 C.)turb ASTM D-4340 0.1561 0.0672 0.1321 0.3002 (mg/cm2/wk) ASTM D-1384115.2 104.7 76.6 87.9 Cu 2.3 0.5 0.5 1.5 ASTM solder −0.6 −1.2 −1.9 −1.7brass 2.2 0.1 0.4 1.8 steel 1.3 −0.2 −0.1 0.6 cast Fe 3.3 2.6 4.2 1.5cast Al 0.4 −2.9 1.8 2.6 ASTM D-2809 (P-I-C) 10-9-9 10-9-10 10-9-9 ASTMD-2570 48.2 94.4 82.7 Cu 7.6 16.8 ASTM solder −1.2 −12.1 −0.5 brass 2.510.8 2.8 steel −0.1 −0.1 0.6 cast Fe −2.4 −1.2 0.6 cast Al −2.8 −3.1−1.9 ASTM D-1881 35/1 25/<1 25/<1 (33%) ml/sec. ASTM D-1882 clearcoat-clearcoat- clearcoat- (conc.) pass non- pass non- pass non- clearcoat-clearcoat- clearcoat- pass pass pass MTU-HSSD 139 mg 172 (mg deposit)deposit Change in pH 9.9 9.8 pH 9.7 9.7 RA 7.24 6.58 RA 7.00 7.31 TTZ293 276 TTZ 284 283 NO₃ 714 718 NO3 764 771 B 326 317 B 324 328 Ca 11217 Ca 114 129 Mg 19 3 Mg 18 19 Na 2478 2404 Na 2543 2652 P 870 777 P 841849 Si 300 107 Si 297 253 Aquatreat Aquatreat Mayoquest MayoquestAR-900-A AR-921-A 1500 1860 RT Stability ok ok ok ok 130 F. Stability okok ok ok 100 C. slight gel sl/mod gel/ moderate lt amber gel GM HardWater Test ok ok ok ok (RT) GM Hard Water Test v v sl ppt v v sl ppt v vsl ppt (82 C.) ASTM D-4340 0.0072 0.0048 (mg/cm2/wk) ASTM D-1384 91.785.8 59.2 Cu 0.9 1.7 6.8 ASTM solder −1.7 −0.4 0.3 brass 1.4 1.7 3.6steel 0.3 1.1 1.0 cast Fe 2.1 3.8 3.7 cast Al 2.0 1.9 13.3 ASTM D-2809(P-I-C) 10-9-9 10-9-9 ASTM D-2570 151.8 96.9 Cu 14.5 15.3 ASTM solder−7.4 −4.0 brass 5.8 8.3 steel 0.8 0.2 cast Fe 1.4 0.7 cast Al −2.1 −2.8ASTM D-1881 25/<1 20/<1 (33%) ml/sec. ASTM D-1882 clearcoat- clearcoat-Coolant A (conc.) pass non- pass non- Control clearcoat- clearcoat-Deionized pass pass Water MTU-HSSD 203 143 mg 10 (mg deposit) depositChange in pH 9.2 9.1 9.2 9.1 pH 10.3 10.1 RA 7.25 7.01 7.21 6.94 RA 6.415.69 TTZ 265 265 268 278 TTZ 288 241 NO₃ 789 778 812 809 NO3 762 653 B343 335 335 329 B 339 280 Ca 117 120 91 120 Ca Mg 18 18 16 19 Mg Na 30022873 2866 2879 Na 2794 1972 P 896 873 857 859 P 882 734 Si 296 259 311271 Si 305 224

Part D HSSD Results

Additional testing was conducted on an HSSD unit. The basic HSSD testmethod consists of cleaning the instrument with an EDTA solution for anhour at a bulk fluid temperature of 140° F. The valve that controls theflow rate is fully opened, and the heater voltage is set at 80V. Theactual test consists of flowing 13 liters of a 50% aqueous coolantsolution at a temperature of 190° F. and at a flow rate of 3 gpm. Theheater voltage is set at 196V. The entire system pressurizes to 8 to 12PSI, which is the natural vapor pressure form heating the water and theglycol. The test solution is run for 96 hours. Examination of the testspecimen surface for scale deposit is visually examined and a sample ofthe before and after test coolant is submitted to analytical foranalysis.

The visual examination of the test specimen surfaces without stabilizingadditives showed that they were covered with a hard water salt scale toan unacceptable degree. The visual examination of the test specimensurfaces with stabilizing additives showed that the surfaces were cleanand were not covered with a hard water salt scale to an visuallyappreciable degree.

Table 3 shows the analytical analysis of the samples. In all cases, thefluid was Coolant A to which the particularly identified stabilizingagents were added as indicated. The runs without the stabilizingadditives have lower total hardness values only because these samplesresulted in unacceptable precipitation throughout the unit that severelyreduced the flow of coolant throughout the system.

TABLE 3 Coolant Flow Run Stabilizing Heater Rinse Total Through #Hardness Agent Deposit Deposit Deposit HSSD unit. 1* 450 ppm None  84 mg 15 mg   99 mg Impeded 2 450 ppm AR-335 167 mg   5 mg   172 mg Unchanged3 450 ppm None  85 mg  54 mg   139 mg Impeded 4  0 ppm None  7 mg 2.5 mg 9.5 mg Impeded 5 450 ppm AR-900 199 mg 3.7 mg 202.7 mg Unchanged 6 450ppm AR-921-A 137 mg 5.6 mg 142.6 mg Unchanged 7 450 ppm None  72 mg  55mg   127 mg Impeded *= Run stopped during the test period

Example 2

Additional stability tests as conducted above in Example 1, Parts A andB were conducted on additional coolants. Coolants B and C were preparedas indicated below in Tables 4 and 5. The stabilizing agents were addedto the particularly identified coolant, i.e, either Coolant B or CoolantC, at a level of 0.1 wt %), based on the total weight of the coolant.

TABLE 4 Coolant B wt. % grams Ethylene Glycol 78.9691 3158.77 NaOH-50%.7348 29.39 NaTT2-50% .5000 20.00 Sodium Benzoate, 15% in EG 16.6667666.67 Tenax WS-5520 .2000 8.00 Corrosion inhibitor 2.000 80.00 H₃PO₄,75% .6001 24.00 -- Anti-Scale -omitted-- [.0893] [3.57] --Colorant-omitted-- [.0400] [1.60] --Additive -omitted-- [.2000] [8.00] 100.00004000.00

TABLE 5 Coolant C wt. % grams Ethylene Glycol 95.6743 3,826.97 Borax,20% in EG 1.9875 79.50 NaOH 50% 1.0528 42.11 H₃PO₄-75% .6602 26.41NaTT2-50% .1165 4.66 Corrosion inhibitor .5000 20.00--Colorant--omitted-- [.0020] [.08] --Additive --omitted-- [.0067] [.27]100.0000 4,000.00

It can be seen from Table 6 and Table 1 that the disclosed stabilizersand coolant compositions function independent of corrosion inhibitor,i.e., whether the corrosion inhibitor comprises silicates and phosphatesas well as additional corrosion inhibitors, i.e., Coolant A, orphosphates and additional corrosion inhibitors, i.e., Coolants B and C.

TABLE 6 Coolant B Coolant C GM Hard Water Test GM Hard Water Test 100°C. (a) RT (24 hr) 82 C. (48 hr) 100° C. RT (24 hr) 82 C. (48 hr) Controlsev floc sev ppt sev ppt sl/mod sev ppt sev ppt crystalline pptAlcosperse 149 mod floc sl turb clear slight floc v sl turb sl turbAlcosperse 240 sev floc sl turb v v sl turb sev floc v sl turb sl turbAlcosperse 420 clear sl turb sl turb clear v sl turb sl turb Alcosperse602-N sev floc v sl turb clear sev floc v sl turb sl turb AquatreatAR-257 clear v sl turb clear clear v sl turb sl turb Aquatreat AR-335clear v v sl turb clear clear v sl turb clear Aquatreat AR-546 sev flocsl turb v sl turb sev floc v sl turb sl turb Aquatreat AR-900-A clear vv sl turb clear clear v sl turb v sl turb Aquatreat AR-921-A mod to sevv v sl turb clear slight floc v sl turb clear floc Aquatreat AR-980 sevfloc sl turb turbid sev floc v sl turb sl turb

1. A coolant concentrate having improved storage stability, theconcentrate consisting of: at least 90 wt % freezing point depressant,based on the total weight of the coolant concentrate; at least onephosphate or the alkali metal or alkaline earth metal salt thereof, andone or more corrosion inhibitors selected from the group consisting oforganic acids; azole type compounds; nitrites, nitrates; borates; andalkali metal or alkaline earth metal salts thereof; at least onestabilizer selected from the group consisting of polyacrylate polymersof the formula:

where R₁ is H; R₄ is a terminating group; X is

and R₂ and R₃ are each independently hydrogen, an alkali metal or analkaline earth metal, and the sum of m and n provide a number averageequivalent weight of less than 6500, and optionally at least oneadditive selected from the group consisting of water, antifoam agents,lubricants, colorants, dispersants, anti-scaling agents, wetting agents,surfactants, pH adjusting and buffering agents.
 2. The concentrate ofclaim 1 wherein R₄ is H or OH.
 3. The concentrate of claim 2 wherein R₄is H.
 4. The concentrate of claim 1 wherein R₂ is an alkali metal or analkaline earth metal.
 5. The concentrate of claim 4 wherein R₂ is analkali metal.
 6. The concentrate as in claim 1 wherein the at least onestabilizer comprises 0.01 wt % to 1.00 wt % of the concentrate, based onthe total weight of the concentrate.
 7. The concentrate of claim 1wherein an organic acid and a nitrite are present in the concentrate. 8.The concentrate of claim 1 wherein the one or more corrosion inhibitorscomprise 0.10 wt % to 10 wt % of the concentrate, based on the totalweight of the concentrate.
 9. The concentrate of claim 1 wherein thefreezing point depressant comprises propylene glycol.
 10. A coolantconsisting of: a freezing point depressant water; at least one phosphateor the alkali metal or alkaline earth metal salt thereof, and one ormore corrosion inhibitors selected from the group consisting of organicacids; azole type compounds; nitrites, nitrates; borates; and alkalimetal or alkaline earth metal salts thereof; at least one stabilizerselected from the group consisting of polyacrylate polymers of theformula:

where R₁ is H; R₄ is a terminating group; X is

and R₂ and R₃ are each independently hydrogen, an alkali metal or analkaline earth metal, and the sum of m and n provide a number averageequivalent weight of less than 6500, and optionally at least oneadditive selected from the group consisting of water, antifoam agents,lubricants, colorants, dispersants, anti-scaling agents, wetting agents,surfactants, pH adjusting and buffering agents.
 11. The concentrate ofclaim 10 wherein R₄ is H or OH.
 12. The concentrate of claim 11 whereinR₄ is H.
 13. The concentrate of claim 10 wherein R₂ is an alkali metalor an alkaline earth metal.
 14. The concentrate of claim 13 wherein R₂is an alkali metal.
 15. The concentrate as in claim 10 wherein the atleast one stabilizer comprises 0.01 wt % to 1.00 wt % of theconcentrate, based on the total weight of the concentrate.
 16. Theconcentrate of claim 10 wherein an organic acid and a nitrite arepresent in the concentrate.
 17. The concentrate of claim 10 wherein theone or more corrosion inhibitors comprise 0.10 wt % to 10 wt % of theconcentrate, based on the total weight of the concentrate.
 18. Theconcentrate of claim 10 wherein the freezing point depressant comprisespropylene glycol.
 19. The concentrate of claim 10 wherein the freezingpoint depressant comprises ethylene glycol, diethylene glycol,1,2-propylene glycol, 1,3-propylene glycol or a combination comprisingtwo or more of the foregoing freezing point depressants.